LIS非线性光学晶体(LiInS2)
所在区域:上海 上海市 浦东新区
更新时间:2017-09-10
品牌:
产品价格:面议
(lithium indium sulphide)
主要特征:
透射范围, µm 0.35- 12.0
非线性系数, pm/V d31=8.35, d32=8.3
对称度 Orthorombic, mm2 point group
晶胞参数, Å a=6.893, b=8.0578, c=6.4816
典型
反射
折射 1064 nm
532 nm nx=2.1305, ny=2.1668, nz=2.1745
nx=2.2353, ny=2.2841, nz=2.2919
用于SHG的基频 x-y, Type II, eoe 2.35 - 6.11
x-z, Type I, ooe 1.78 - 8.22
y-z, Type II, oeo 2.35 - 2.67
y-z Type II, oeo 5.59 - 6.11
Total interval covered 1.617 - 8.71
光学损伤阈值 GW/cm2 1053 nm
(t=10 ns) ~1
热导率k, WM/M°C kx=6.1 ± 0.3; ky=5.9 ± 0.3; kz=7.4 ± 0.3
Absorption edge in the far-IR on 0.2transparency level 2.58 THz at 118 µm
主要特征:
透射范围, µm 0.35- 12.0
非线性系数, pm/V d31=8.35, d32=8.3
对称度 Orthorombic, mm2 point group
晶胞参数, Å a=6.893, b=8.0578, c=6.4816
典型
反射
折射 1064 nm
532 nm nx=2.1305, ny=2.1668, nz=2.1745
nx=2.2353, ny=2.2841, nz=2.2919
用于SHG的基频 x-y, Type II, eoe 2.35 - 6.11
x-z, Type I, ooe 1.78 - 8.22
y-z, Type II, oeo 2.35 - 2.67
y-z Type II, oeo 5.59 - 6.11
Total interval covered 1.617 - 8.71
光学损伤阈值 GW/cm2 1053 nm
(t=10 ns) ~1
热导率k, WM/M°C kx=6.1 ± 0.3; ky=5.9 ± 0.3; kz=7.4 ± 0.3
Absorption edge in the far-IR on 0.2transparency level 2.58 THz at 118 µm